Nitric oxide microsensors via fluorosilane-based xerogel membranes

ABSTRACT

The presently disclosed subject matter relates to sensors for measuring an amount of a gaseous species in a sample. The sensors comprise a gas permeable polysiloxane network membrane, comprising both alkyl and fluorinated alkyl groups. In some embodiments, the polysiloxane network can be formed from the co-condensation of a mixture of an alkylalkoxysilane and a fluorosilane. The presently disclosed subject matter also relates to methods of making the sensors, methods of selectively measuring an amount of a gaseous species, such as nitric oxide, in a sample, and to compositions comprising the polysiloxane networks.

RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional PatentApplication Ser. No. 60/839,870, filed Aug. 24, 2006; the disclosure ofwhich is incorporated herein by reference in its entirety.

GOVERNMENT INTEREST

This invention was made with U.S. Government support from NationalInstitutes of Health Grant Number EB000708. Thus, the U.S. Governmenthas certain rights in the invention.

TECHNICAL FIELD

The presently disclosed subject matter relates to sensors comprising agas permeable membrane comprising alkyl and fluorinated alkyl groups.The sensors can be used as biosensors for the detection and measurementof biologically relevant gaseous species, including nitric oxide andoxygen. Also provided are methods for making the sensors, methods ofmeasuring an amount of a gaseous species in a sample, and compositionscomprising polysiloxane networks having alkyl and fluorinated alkylsubstituents.

ABBREVIATIONS

-   -   atm=atmosphere    -   BTMOS=butyltrimethoxysilane    -   ° C.=degrees Celsius    -   EtOH=ethanol    -   g=grams    -   h=hours    -   HTMOS=hexyltrimethoxysilane    -   MeOH=methanol    -   mg=milligrams    -   min=minutes    -   μL=microliters    -   mL=milliliters    -   μm=micrometers    -   μM=micromolar    -   mm=millimeters    -   MRI=magnetic resonance imaging    -   MTMOS=methyltrimethoxysilane    -   nA=nanoampere    -   nm=nanometers    -   nM=nanomolar    -   NMR=nuclear magnetic resonance    -   NO=nitric oxide    -   NO₂ ⁻=nitrite    -   NOS=nitric oxide synthase    -   OTMOS=octyltrimethoxysilane    -   pA=picoampere    -   pM=picomolar    -   PBS=phosphate-buffered saline    -   Pt=platinum

BACKGROUND

Nitric oxide (NO) is a diatomic free radical endogenously synthesized inthe human body when L-arginine is converted to L-citrulline by a classof enzymes known as nitric oxide synthases (NOS's). Since the firstreports describing NO's action as an endothelium-derived relaxationfactor, much research has been devoted to elucidating the pathways of NOgeneration and action in biological milieu. In particular, NO isinvolved in neurotransmission, vasodilation, immune responses (includinganti-tumor and anti-microbial activities), the inhibition of plateletaggregation, and in blood pressure control. See Zhang, X., Frontiers inBioscience, 9, 3434-3446 (2004).

Miniaturized electrochemical sensors represent promising devices fordetermining the spatial and temporal distributions of NO in physiology.The use of such sensors, however, has been limited by low sensitivity,comparatively slow response time, and/or interferences from otherreadily oxidizable biological species (e.g., nitrite, ascorbic acid,uric acid, and dopamine).

In attempts to address these limitations, a variety of permselectivepolymers have been synthesized and employed as sensor membranes. Forexample, poly(tetrafluoroethylene) (TEFLON®, E. I. du Pont de Nemoursand Company, Wilmington, Del., United States of America) has proven tobe a selective membrane resulting in the fabrication of nitric oxidesensors with good sensitivity. Unfortunately, the poor solubility ofpoly(tetrafluoroethylene) in standard organic solvents and the intricateprocess required to mount or coat such films onto electrodes hashindered its utility as a membrane for fabricating microsensors,including those for use in detecting and measuring nitric oxide.

Accordingly, there is a need in the art for gas permeable materials foruse as sensor membranes. In particular, there is a need for gaspermeable materials that can be synthesized using common solvents andvia methods that can be readily modified to tailor the permeability andselectivity of the materials for a specific use and to easily coat avariety of sensor shapes and materials.

SUMMARY

In some embodiments, the presently disclosed subject matter provides asensor for measuring an amount of a gaseous species in a sample, thesensor comprising:

-   -   (a) an electrode assembly;    -   (b) a gas permeable membrane located between one or more        surfaces of the electrode assembly and the sample, wherein the        membrane comprises a polysiloxane network wherein one or more        silicon atoms in the polysiloxane network is covalently attached        to an alkyl group and one or more silicon atoms in the        polysiloxane network is covalently attached to a fluorinated        alkyl group; and    -   (c) a detector for measuring current at the electrode assembly.

In some embodiments, the gaseous species is selected from nitric oxideand oxygen.

In some embodiments, the electrode assembly is selected from the groupconsisting of:

an electrode assembly comprising a working electrode;

an electrode assembly comprising a working electrode and a referenceelectrode; and

an electrode assembly comprising a working electrode, a referenceelectrode, and a counter electrode.

In some embodiments, the working electrode comprises a material selectedfrom platinum, platinized platinum, tungsten, gold, carbon, carbonfiber, and combinations thereof. In some embodiments, the referenceelectrode comprises silver/silver chloride. In some embodiments, thecounter electrode comprises platinum.

In some embodiments, the polysiloxane network is a condensation productof a silane mixture comprising an alkylalkoxysilane and a fluorosilane.

In some embodiments, the fluorosilane comprises a structure having aformula:

F₃C—(CF₂)_(m)—(CH₂)_(n)—Si(X)_(p)(Y)_(3-p)

wherein:

m is 0 to 15;

n is 1 to 5;

p is 1, 2, or 3;

each X is independently selected from the group consisting of alkoxy,aryloxy, aralkoxy, hydroxyl, and halo; and

each Y is independently selected from the group consisting of H, alkyl,aryl, and aralkyl.

In some embodiments, the fluorosilane is selected from the groupconsisting of:

-   (3,3,3-trifluoropropyl)trimethoxysilane;-   nonafluorohexyltrimethyoxysilane;-   nonafluorohexyltriethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane;-   (perfluoroalkyl)ethyltriethoxysilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane; and    combinations thereof.

In some embodiments, the alkylalkoxysilane is selected from the groupconsisting of:

methyltrimethoxysilane (MTMOS);

ethyltrimethoxysilane;

propyltrimethoxysilane;

butyltrimethoxysilane (BTMOS);

hexyltrimethoxysilane (HTMOS);

octyltrimethoxysilane (OTMOS); and

combinations thereof.

In some embodiments, the silane mixture comprises about 1% to about 99%by volume fluorosilane. In some embodiments, the silane mixturecomprises about 5% to about 50% by volume fluorosilane. In someembodiments, the silane mixture comprises about 20% by volumefluorosilane.

In some embodiments, the silane mixture comprises about 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane and about 80%by volume methyltrimethoxysilane.

In some embodiments, the sensor comprises an internal electrolyte layer,wherein the internal electrolyte layer is located between the electrodeassembly and the gas permeable membrane. In some embodiments, theinternal electrolyte layer is a hydrogel composition. In someembodiments, the hydrogel composition comprises poly(vinylpyrrolidone).

In some embodiments, the presently disclosed subject matter provides amethod of making a sensor for measuring an amount of a gaseous speciesin a sample, the method comprising:

(a) providing a silane mixture comprising a fluorosilane and analkylalkoxysilane;

(b) providing an electrode assembly;

(c) coating at least one portion of the electrode assembly with thesilane mixture to form a coated electrode; and

(d) drying the coated electrode to form a gas permeable polysiloxanemembrane layer on at least one portion of the electrode assembly.

In some embodiments, the silane mixture is dissolved in a solvent. Insome embodiments, the solvent comprises an alcohol and water. In someembodiments, the alcohol is ethanol.

In some embodiments, the solvent comprises a catalyst. In someembodiments, the catalyst is hydrochloric acid.

In some embodiments, the drying takes place at ambient temperature. Insome embodiments, the drying takes place at an elevated temperature. Insome embodiments, the drying step further comprises exposing themembrane layer to one of nitric oxide or argon at a pressure.

In some embodiments, the coating is performed by dipping the electrodeassembly into the silane mixture.

In some embodiments, the method further comprises repeating the coatingand drying steps one or more times to provide a thicker membrane layer.

In some embodiments, prior to coating the at least one portion of theelectrode assembly with the silane mixture, the at least one portion ofthe electrode assembly is coated with a hydrogel material.

In some embodiments, the presently disclosed subject matter provides asensor prepared by a method comprising:

(a) providing a silane mixture comprising a fluorosilane and analkylalkoxysilane;

(b) providing an electrode assembly;

(c) coating at least one portion of the electrode assembly with thesilane mixture to form a coated electrode; and

(d) drying the coated electrode to form a gas permeable polysiloxanemembrane layer on at least one portion of the electrode assembly.

In some embodiments, the presently disclosed subject matter provides amethod of measuring an amount of a gaseous species in a sample, themethod comprising contacting the sample with a sensor comprising apolysiloxane membrane, wherein the polysiloxane membrane comprises oneor more silicon atoms covalently attached to an alkyl group and one ormore silicon atoms covalently attached to a fluorinated alkyl group, andfurther wherein the polysiloxane membrane selectively allows the gaseousspecies in the sample to be measured by the sensor.

In some embodiments, the sensor is an amperometric sensor.

In some embodiments, the polysiloxane membrane is positioned between thesample and an electrode assembly.

In some embodiments, the sample is a biological sample or anenvironmental sample. In some embodiments, the biological sample isselected from a cell, a tissue, a biological fluid, or an extractthereof. In some embodiments, the sample comprises brain cells,macrophages, neutrophils, or blood. In some embodiments, the sample isin a living subject. In some embodiments, the sample is in the brain ofa living subject. In some embodiments, the sample comprises a singlecell.

In some embodiments, the gaseous species is nitric oxide or oxygen. Insome embodiments, the gaseous species is measured at a concentration aslow as 200 pM.

In some embodiments, the presently disclosed subject matter provides acomposition comprising a polysiloxane network, wherein one or moresilicon atom in the polysiloxane network is covalently attached to analkyl group and one or more silicon atom in the polysiloxane network iscovalently attached to a fluorinated alkyl group having a structure of:

wherein m is 0 to 15 and n is 1 to 5.

In some embodiments, each silicon atom in the polysiloxane network iscovalently attached to an alkyl group or to a fluorinated alkyl group.

In some embodiments, the polysiloxane network is selectively permeableto a biologically relevant gaseous species. In some embodiments, thebiologically relevant gaseous species is selected from the groupconsisting of nitric oxide and oxygen.

In some embodiments, the polysiloxane network is a condensation productof a silane mixture comprising an alkylalkoxysilane and a fluorosilane.In some embodiments, the polysiloxane network is formed by a sol-gelprocess.

Thus, it is an object of the presently disclosed subject matter toprovide sensors, compositions, and methods related to measuring anamount of a gaseous species in a sample.

An object of the presently disclosed subject matter having been statedherein above, which are addressed in whole or in part by the presentlydisclosed subject matter, other objects and aspects will become evidentas the description proceeds when taken in connection with theaccompanying Examples as best described herein below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a schematic illustration of a longitudinal cross view of anelectrode assembly comprising a xerogel membrane-coated sensing tip.

FIG. 1B is a schematic illustration of a top view of the sensing end ofthe electrode described in FIG. 1A, shown in the absence of anyelectrode assembly tip coatings.

FIG. 2A is a scanning electron micrograph of a platinizedtungsten-platinum wire microelectrode. An approximately 53 μm longsection of the tapered end portion of the microelectrode is coated byplatinum black. The tip of the microelectrode has a diameter of 5 μm.The scale marking in the bottom right-hand corner of the micrographrepresents 50 μm.

FIG. 2B is a scanning electron micrograph of the microelectrodedescribed for FIG. 2A, showing the rough, platinized tip region of themicroelectrode under higher magnification.

FIG. 2C is a schematic illustration of the tip region of the platinizedtungsten-platinum wire microelectrode shown in FIGS. 2A and 2B. Themicroelectrode comprises an inner tungsten core covered by a layer ofplatinum. The platinum layer is further coated with a layer of platinumblack (i.e., a rough platinum coating).

FIG. 3 is a composite graph showing the nitric oxide (NO) permeability(bar graph, for left axis) and selectivity over nitrite (NO₂ ⁻) (scatterplots, for right axis) of xerogel membranes of varying chemicalcomposition coated on platinum macroelectrodes. The xerogel membraneswere prepared from a mixture of 80% by volume methyltrimethoxysilane(MTMOS) and 20% by volume fluorosilane (i.e.,(3,3,3-trifluoropropyl)trimethoxysilane (3FTMS),nonafluorohexyltrimethoxysilane (9FTMS),(tridecafluoro-1,1,2,2-tetrahydrooctyl)-trimethoxysilane (13FTMS) or(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane (17FTMS)). Thedashed line indicates nitric oxide over nitrite selectivity of the barePt electrode.

FIG. 4 is a composite graph of the dynamic response and calibration(inset) curves of a platinized platinum (Pt) microelectrode coated witha membrane comprising a co-condensed network of a silane mixturecomprising 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (remaindermethyltrimethoxysilane, (MTMOS)). The curves show the response of thecoated microelectrode to nitric oxide at concentrations between 30 nMand 1200 nM (as indicated by the captions and arrows). The right-handside of the dynamic response curve also shows the response of the coatedmicroelectrode to nitrite (NO₂ ⁻) at concentrations between 2 μM and 25μM (also as indicated by the captions and arrows).

FIG. 5 is a composite graph showing expansions of the dynamic responseand calibration (inset) curves shown in FIG. 4 at nitric oxideconcentrations between 30 nM and 300 nM. The slope of the calibrationcurve is −9.96 pA/nM; linearity (r)=0.9987.

FIG. 6A is the dynamic response curve of the coated microelectrodedescribed in FIG. 4 at nitric oxide concentrations between 0.5 μM and4.0 μM.

FIG. 6B is the calibration curve corresponding to the dynamic responsecurve shown in FIG. 6A. The slope is −7.60 nA/μM; the linearity(r)=0.9999.

FIG. 7A is a dynamic response curve of a non-coated platinized platinummicroelectrode at nitric oxide concentrations between 0.5 μM and 4.0 μM.

FIG. 7B is the calibration curve corresponding to the dynamic responsecurve shown in FIG. 7A. The slope is −11.57 nA/μM, the linearity is0.9999.

FIG. 8 is a composite graph of the dynamic response and calibration(inset) curves of the coated microelectrode described in FIG. 4 atnitric oxide concentrations between 200 pM and 3 nM (as indicated by thecaptions and arrows). The right-hand side of the dynamic response curvealso shows the response of the coated microelectrode to nitrite (NO₂ ⁻)at concentrations between 1 μM and 5 μM (also as indicated by thecaptions and arrows).

FIG. 9 is a composite graph of the dynamic response (inset) andcalibration curves of a macroelectrode coated with a membrane comprisinga co-condensed network of a silane mixture comprising 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (remainder(i.e., 80% by volume) methyltrimethoxysilane, (MTMOS)). The calibrationcurve shows that the coated macroelectrode has a linear response tooxygen gas (O₂) at concentrations between 36 and 360 mmHg (slope=44.7nA/mmHg; r=0.9908). The dynamic response curve also shows the responseof the coated macroelectrode to O₂ at concentrations of 36, 72, 151, and360 mmHg (as indicated by the captions and arrows).

FIG. 10 is a bar graph showing porcine platelet adhesion toxerogel-coated glass slides. The bar indicated by 17FTMOS refers to aglass slide coated with a xerogel comprising a co-condensed network of asilane mixture comprising 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (remainder(i.e., 80% by volume) methyltrimethoxysilane (MTMOS)). The bar indicatedby MTMOS refers to a glass slide coated with a xerogel prepared by thecondensation of MTMOS. Values were determined relative to plateletadhesion observed for an uncoated glass slide.

DETAILED DESCRIPTION

The presently disclosed subject matter will now be described more fullyhereinafter with reference to the accompanying Examples, in whichrepresentative embodiments are shown. The presently disclosed subjectmatter can, however, be embodied in different forms and should not beconstrued as limited to the embodiments set forth herein. Rather, theseembodiments are provided so that this disclosure will be thorough andcomplete, and will fully convey the scope of the embodiments to thoseskilled in the art.

Unless otherwise defined, all technical and scientific terms used hereinhave the same meaning as commonly understood by one of ordinary skill inthe art to which this presently described subject matter belongs. Allpublications, patent applications, patents, and other referencesmentioned herein are incorporated by reference in their entirety.

Throughout the specification and claims, a given chemical formula orname shall encompass all optical and stereoisomers, as well as racemicmixtures where such isomers and mixtures exist.

I. DEFINITIONS

Following long-standing patent law convention, the terms “a” and “an”mean “one or more” when used in this application, including the claims.

The term “about,” as used herein, when referring to a value or to anamount of mass, weight, time, volume, diameter, or percentage is meantto encompass variations of ±20% or ±10%, more preferably ±5%, even morepreferably ±1%, and still more preferably ±0.1% from the specifiedamount, as such variations are appropriate to perform the disclosedmethod.

The term “hydrophobic” refers to a chemical compound or moiety that, toa given extent, repels or does not interact with water throughnon-covalent forces such as hydrogen bonding or electrostaticinteractions. A compound can be strongly hydrophobic or slightlyhydrophobic. The calculated dielectric constant of a compound or groupcan be used to predict the level or degree of hydrophobicity of thecompound or moiety. Compounds or moieties with lower dielectricconstants will be more hydrophobic.

The term “porous” refers to a material having pores. The material can bemesoporous, comprising pores in the range of between about 20-500angstroms. The material can be macroporous and comprise pores having adiameter greater than about 50 nm.

As used herein the term “alkyl” refers to C₁-C₂₀ inclusive, linear(i.e., “straight-chain”), branched, or cyclic, saturated or at leastpartially and in some cases fully unsaturated (i.e., alkenyl andalkynyl)hydrocarbon chains, including for example, methyl, ethyl,propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl, hexyl, octyl,ethenyl, propenyl, butenyl, pentenyl, hexenyl, octenyl, butadienyl,propynyl, butynyl, pentynyl, hexynyl, heptynyl, and allenyl groups.“Branched” refers to an alkyl group in which a lower alkyl group, suchas methyl, ethyl or propyl, is attached to a linear alkyl chain.Exemplary branched alkyl groups include, but are not limited to,isopropyl, isobutyl, tert-butyl, “Lower alkyl” refers to an alkyl grouphaving 1 to about 8 carbon atoms (i.e., a C₁₋₈ alkyl), e.g., 1, 2, 3, 4,5, 6, 7, or 8 carbon atoms. “Higher alkyl” refers to an alkyl grouphaving about 10 to about 20 carbon atoms, e.g., 10, 11, 12, 13, 14, 15,16, 17, 18, 19, or 20 carbon atoms. In certain embodiments, “alkyl”refers, in particular, to C₁₋₈ straight-chain alkyls. In otherembodiments, “alkyl” refers, in particular, to C₁₋₈ branched-chainalkyls.

Alkyl groups can optionally be substituted (a “substituted alkyl”) withone or more alkyl group substituents, which can be the same ordifferent. The term “alkyl group substituent” includes but is notlimited to alkyl, substituted alkyl, halo, arylamino, acyl, hydroxyl,aryloxyl, alkoxyl, alkylthio, arylthio, aralkyloxyl, aralkylthio,carboxyl, alkoxycarbonyl, oxo, and cycloalkyl. There can be optionallyinserted along the alkyl chain one or more oxygen, sulfur or substitutedor unsubstituted nitrogen atoms, wherein the nitrogen substituent ishydrogen, lower alkyl (also referred to herein as “alkylaminoalkyl”), oraryl.

Thus, as used herein, the term “substituted alkyl” includes alkylgroups, as defined herein, in which one or more atoms or functionalgroups of the alkyl group are replaced with another atom or functionalgroup, including for example, alkyl, substituted alkyl, halogen, aryl,substituted aryl, alkoxyl, hydroxyl, nitro, amino, alkylamino,dialkylamino, sulfate, and mercapto. In some embodiments, thesubstituted alkyl group is a fluorinated alkyl group.

The term “fluorinated alkyl” refers to an alkyl group (i.e., C₁-C₂₀linear, branched, or cyclic alkyl) wherein one or more of the C—H bondsare replaced by C—F bonds. In some embodiments, the entire length or aportion of the entire length (i.e., several consecutive carbon atoms) ofthe alkyl group is perfluorinated (i.e., each of the C—H bonds isreplaced by a C—F bond).

The term “aryl” is used herein to refer to an aromatic substituent thatcan be a single aromatic ring, or multiple aromatic rings that are fusedtogether, linked covalently, or linked to a common group, such as, butnot limited to, a methylene or ethylene moiety. The common linking groupalso can be a carbonyl, as in benzophenone, or oxygen, as indiphenylether, or nitrogen, as in diphenylamine. The term “aryl”specifically encompasses heterocyclic aromatic compounds. The aromaticring(s) can comprise phenyl, naphthyl, biphenyl, diphenylether,diphenylamine and benzophenone, among others. In particular embodiments,the term “aryl” means a cyclic aromatic comprising about 5 to about 10carbon atoms, e.g., 5, 6, 7, 8, 9, or 10 carbon atoms, and including 5and 6-membered hydrocarbon and heterocyclic aromatic rings.

The aryl group can be optionally substituted (a “substituted aryl”) withone or more aryl group substituents, which can be the same or different,wherein “aryl group substituent” includes alkyl, substituted alkyl,aryl, substituted aryl, aralkyl, hydroxyl, alkoxyl, aryloxyl,aralkyloxyl, carboxyl, acyl, halo, nitro, alkoxycarbonyl,aryloxycarbonyl, aralkoxycarbonyl, acyloxyl, acylamino, aroylamino,carbamoyl, alkylcarbamoyl, dialkylcarbamoyl, arylthio, alkylthio,alkylene, and —NR′R″, wherein R′ and R″ can each be independentlyhydrogen, alkyl, substituted alkyl, aryl, substituted aryl, and aralkyl.

Thus, as used herein, the term “substituted aryl” includes aryl groups,as defined herein, in which one or more atoms or functional groups ofthe aryl group are replaced with another atom or functional group,including for example, alkyl, substituted alkyl, halogen, aryl,substituted aryl, alkoxyl, hydroxyl, nitro, amino, alkylamino,dialkylamino, sulfate, and mercapto.

Specific examples of aryl groups include, but are not limited to,cyclopentadienyl, phenyl, furan, thiophene, pyrrole, pyran, pyridine,imidazole, benzimidazole, isothiazole, isoxazole, pyrazole, pyrazine,triazine, pyrimidine, quinoline, isoquinoline, indole, carbazole,fluorene, and the like.

“Aralkyl” refers to an aryl-alkyl- group wherein aryl and alkyl are aspreviously described, and included substituted aryl and substitutedalkyl. Exemplary aralkyl groups include benzyl, phenylethyl, andnaphthylmethyl.

“Alkoxyl” refers to an alkyl-O— group wherein alkyl is as previouslydescribed. The term “alkoxyl” as used herein can refer to, for example,methoxyl, ethoxyl, propoxyl, isopropoxyl, butoxyl, t-butoxyl, andpentoxyl. The terms “oxyalkyl” and “alkoxy” can be used interchangeablywith “alkoxyl”.

“Aryloxyl” and “aryloxy” refer to an aryl-O— group wherein the arylgroup is as previously described, including a substituted aryl. The term“aryloxyl” as used herein can refer to phenyloxyl or hexyloxyl, andalkyl, substituted alkyl, halo, or alkoxyl substituted phenyloxyl orhexyloxyl.

“Aralkyloxyl,” “aralkoxy,” and “aralkyloxy” refer to an aralkyl-O— groupwherein the aralkyl group is as previously described. An exemplaryaralkyloxyl group is benzyloxyl.

The terms “halo”, “halide”, or “halogen” as used herein refer to fluoro,chloro, bromo, and iodo groups.

The term “hydroxyl” and “hydroxy” refer to the —OH group.

The term “hydroxyalkyl” refers to an alkyl group substituted with an —OHgroup.

The terms “silyl” and “silane” refer to chemical groups and compoundscomprising silicon atoms (Si).

As used herein the term “alkoxysilane” refers to a compound comprisingone, two, three, or four alkoxy groups bonded to a silicon atom. Forexample, tetraalkoxysilane refers to Si(OR)₄, wherein R is alkyl. Eachalkyl group can be the same or different.

An “alkylalkoxysilane” refers to an alkoxysilane wherein one, two orthree of the alkoxy groups has been replaced with an alkyl group (i.e.,a R′—Si(OR)₃ group, a R′₂—Si(OR)₂ group or a R′₃—Si(OR) group). Eachalkyl group can be the same or different. Thus, an alkylalkoxysilanecomprises at least one carbon-Si bond.

The term “fluorosilane” refers to a silane comprising one or morefluorine atoms. In some embodiments, the fluorosilane is a compoundcomprising a silicon atom attached to at least one fluorinated alkylgroup. In some embodiments, the fluorosilane comprises a compound of theformula R″Si(X)_(p)(Y)_(3-p), wherein p is an integer from 1-3; R″ is afluorinated alkyl group, each X is a hydrolyzable group (e.g., alkoxy,aryloxy, aralkoxy, hydroxyl or halo), and each Y is H, alkyl, aryl, oraralkyl. In some embodiments, p is 3 and the fluorosilane comprises acompound of the formula R″Si(X)₃. In some embodiments, each X group isselected from alkoxy, hydroxyl, and halo. In some embodiments, each X isethoxy, methoxy or chloro.

The term “silanol” refers to the —Si—OH group.

The term “polysiloxane” refers to a polymeric material comprising abackbone of silicon-oxygen bonds (i.e., —Si—O—Si—O—Si—) having theformula R_(n)SiX_(y)O_(m), wherein each R is an H, alkyl, aryl, aralkyl,or substituted alkyl group and each X is an alkoxy, aryloxy, aralkoxy,hydroxyl or halo group. In some embodiments, each silicon atom iscovalently bonded to one R group, for example one alkyl or fluorinatedalkyl group. Each silicon atom is also crosslinked to one, two, or threeother silicon atoms via silicon-oxygen bonds and bonded to zero, one, ortwo X groups, such as ethoxy, methoxy, hydroxyl, or chloro. Thus, insome embodiments, higher the level of crosslinking in the polysiloxane,the fewer X groups are present. The terms “polysiloxane” and “silicone”can be used interchangeably.

As used herein, the term “oxygen” when referring to a gas, refers todioxygen, i.e., O₂.

The term “co-condensation” and “co-condensed” refer to materials thatare formed when two different compounds (such as, for example, afluorosilane and an alkylalkoxysilane) react with each other to form athird compound and to give off a molecule or molecules of an alcohol orwater.

The term “xerogel” as used herein refers to a polymeric network formedvia a sol-gel process. In particular, the term xerogel can be used torefer to polysiloxane networks formed from the co-condensation ofsolutions containing silane mixtures.

The term “permselective” refers to selective permeability, for example,of a material, such as a membrane. Thus, a permselective or selectivelypermeable membrane allows some molecules to pass through the membrane,while other molecules cannot pass through the membrane. In someembodiments, the term “permselective” as used herein refers to amembrane that selectively allows small, nonpolar gaseous molecules topass through, while being impermeable to larger or more polar molecules.

Thus, in some embodiments, the permselective or selectively permeablematerial or membrane is selectively permeable to nitric oxide andoxygen, while not being permeable to compounds such as nitrite (NO₂ ⁻),ascorbic acid, uric acid, acetaminophen, dopamine, and aqueous liquids.

II. POLYSILOXANE COMPOSITIONS

In some embodiments, the presently disclosed subject matter provides apolysiloxane network comprising at least one silicon atom having analkyl group substituent and at least one silicon atom having afluorinated alkyl group substituent, wherein the fluorinated alkyl grouphas the structure:

wherein m is 0 to 15 and n is 1 to 5. In some embodiments, each of thesilicon atoms in the polysiloxane network is covalently attached toeither an alkyl group or to a fluorinated alkyl group.

In some embodiments, the polysiloxane network is selectively permeableto a biologically relevant gaseous species, for example, to nitric oxideand/or oxygen (O₂).

In some embodiments, the polysiloxane network is a co-condensed productof a silane mixture comprising an alkylalkoxysilane and a fluorosilane.

In some embodiments, the fluorosilane comprises a structure having aformula:

F₃C—(CF₂)_(m)—(CH₂)_(n)—Si(X)_(p)(Y)_(3-p)

wherein:

m is 0 to 15;

n is 1 to 5;

p is 1, 2, or 3;

each X is independently selected from the group consisting of alkoxy,aryloxy, aralkoxy, hydroxyl, and halo; and

each Y is independently selected from the group consisting of H, alkyl,aryl, and aralkyl.

Thus, the fluorosilane can comprise a fluorinated alkyl group and atleast one hydrolyzable group that can take place in a condensationreaction. The silicon atom of the fluorosilane can also be attached toone or two non-fluorinated, non-hydrolyzable groups. In someembodiments, p is 2 and the fluorosilane can comprise two X groups andone Y group. In some embodiments, p is 1 and the fluorosilane cancomprise one X group and two Y groups.

In some embodiments, each of the silicon atom substituents of thefluorosilane is either a fluorinated alkyl group or a hydrolyzablegroup. Thus, in some embodiments, p is 3, and the fluorosilane can havethe formula:

F₃C—(CF₂)_(m)—(CH₂)_(n)—Si(X)₃.

In some embodiments, each X is independently alkoxy or halo. For inexample, each X can be ethoxy, methoxy, or chloro. In some embodiments,each Y is alkyl.

In some embodiments, the fluorosilane is selected from the groupconsisting of:

-   (3,3,3-trifluoropropyl)trimethoxysilane;-   nonafluorohexyltrimethyoxysilane;-   nonafluorohexyltriethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane;-   (tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane;-   (perfluoroalkyl)ethyltriethoxysilane;-   (heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane; and    combinations thereof.

In some embodiments, the alkylalkoxysilane is selected from the groupconsisting of: methyltrimethoxysilane (MTMOS); ethyltrimethoxysilane;propyltrimethoxysilane; butyltrimethoxysilane (BTMOS);hexyltrimethoxysilane (HTMOS); octyltrimethoxysilane (OTMOS); andcombinations thereof.

In some embodiments, the silane mixture comprises about 1% to about 99%by volume fluorosilane. In some embodiments, the silane mixturecomprises about 5% to about 50% by volume fluorosilane. In someembodiments, the silane mixture comprises about 20% by volumefluorosilane. In some embodiments, the silane mixture comprises about20% by volume (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilaneand about 80% by volume methyltrimethoxysilane.

In some embodiments, the polysiloxane network is a xerogel formed usinga sol-gel polymerization process. In a sol-gel process, precursors ofthe polysiloxane network (e.g., the alkylalkoxysilane and thefluorosilane) are present in a solution. For example, the precursors canbe dissolved in a solvent. The solvent can comprise water and analcohol, such as, ethanol, methanol, propanol, and the like. Aspolymerization proceeds, the precursors bond to one another, forming amacromolecule (i.e., a gel).

The “sol-gel” process of forming the polysiloxane network can involvetwo types of chemical reactions. The first step involves a hydrolysisreaction in which an alkoxy or chloro group of an alkylalkoxysilaneand/or a fluorosilane is hydrolyzed, thereby forming a silanol group(i.e., a hydroxy group attached to the Si atom). The hydrolysis reactioncan be catalyzed by Bronstead acids or bases (i.e., groups that generateH⁺ or OH⁻ ions), such as, for example, acetic acid or hydrochloric acid.The second step is a condensation reaction wherein two silanols or asilanol and an alkoxysilane react to form a siloxane bond (i.e.,Si—O—Si) while releasing a molecule of water or a molecule of analcohol.

The presently disclosed fluorosilane-based materials can be analyzedusing solid state ²⁹Si NMR, using surface wettability measurements, andusing electrochemical techniques to monitor changes in the chemicalstructure of the xerogel as a function of precursor composition andprocessing conditions.

For example, the level of co-condensation in the polymeric silane-basednetwork can be monitored using solid state ²⁹Si NMR by assessing changesin relative amounts of NMR peaks associated with three different typesof silyl group, which are illustrated below in Scheme 1. One type ofsilyl group comprises two hydroxyl groups (structure A in Scheme 1), oneR group (i.e., an alkyl or fluorinated alkyl group) and is attached tothe co-condensed silicone network via one siloxane bond (as indicated bythe wavy line). A second type of silyl group comprises one hydroxylgroup, one R group, and has two attachment sites to the network(structure B). A third type of silyl group (structure C) comprises threeattachment sites to the network and one R group.

Xerogel stability to various potential use conditions can also betested. For instance, a xerogel membrane can be soaked in a solution ata given pH or temperature for a period of time, and the Si concentrationin the solution can be measured (e.g. using direct current plasmaoptical emission spectroscopy) to determine the amount of membranefragmentation. The xerogels can also be tested to determine theirpermselectivity to particular gaseous or non-gaseous species ofinterest. In certain embodiments, it can be desirable to determine thebiocompatibility of the presently disclosed fluorosilane-based xerogelmembranes, depending upon the desired end use of the membranes or thedevices prepared with the membranes. Thus, in some embodiments, thexerogel can be tested to determine its immunogenicity and/or itsaffinity for antibodies, proteins, and/or other biological componentsthat can be present in mammalian cells, tissues or fluids.

For example, when the presently disclosed fluorosilane-based xerogelmembranes are to be in contact with blood (e.g., in intravenous use), itcan be desirable to assess and/or tailor the thromboresistivity of themembranes. In some embodiments, thromboresistivity can be assessedaccording to the membrane's ability to resist platelet adhesion using anin vitro platelet adhesion assay. Marxer, S. M., et al., Analyst, 130,206-212 (2005). Factors that can change from xerogel to xerogel, such aswettability and surface roughness, are believed to be able to affectmembrane thromboresistivity. See Marxer, S. M. et al., Analyst, 130,206-212 (2005). Surface wettability of a membrane can be determined bymeasuring the water contact angles of a membrane, for instance, beforeand after exposure to water for one or more periods of time. Surfaceroughness can be assessed via microscopy, such as atomic forcemicroscopy or any other suitable microscopy method. See Marxer, S. M.,et al., Analyst, 130, 206-212 (2005).

III. SENSORS

The presently disclosed subject matter provides sensors comprising gaspermeable membranes comprising polysiloxane networks. The polysiloxanenetworks comprise both alkyl and fluorinated alkyl groups.

Generally, the presently disclosed sensors can detect the presence ofthe gaseous species using an electrochemical technique, such as avoltammetric or coulometric technique. In some embodiments, the sensoris an amperometric sensor (i.e., it detects the redox current producedby the oxidation of the gaseous species over time at a fixed voltagepotential). In some embodiments, the detector is a potentiostat.

Thus, in some embodiments, the presently disclosed subject matterprovides a sensor for measuring an amount of a gaseous species in asample, the sensor comprising:

(a) an electrode assembly;

(b) a gas permeable membrane located between one or more surfaces of theelectrode assembly and the sample, wherein the membrane comprises apolysiloxane network wherein one or more silicon atoms in thepolysiloxane network is covalently attached to an alkyl group and one ormore silicon atoms in the polysiloxane network is covalently attached toa fluorinated alkyl group; and

(c) a detector for measuring current at the electrode assembly.

In some embodiments, the gaseous species is selected from nitric oxideand oxygen. In some embodiments, the membrane is selectively permeableto one or more of nitric oxide and oxygen. Thus, in some embodiments,the presently disclosed sensors comprise membranes that are macro- ormeso-porous, and allow some molecules to pass into or through themembrane. Other molecules cannot pass through the membrane because oftheir size or because of electrostatic repulsion with the membranematerial. In particular, without being bound to any one particulartheory, because the presently described polysiloxane network membranesare composed of silanes having non-hydrophilic substituents (i.e., alkylor fluorinated alkyl groups), in some embodiments, the networks areselectively permeable to neutral molecules (e.g., NO and O₂) incomparison with charged species (e.g., nitrite (NO₂ ⁻)).

The electrode assembly can comprise one, two, three, or more electrodes.In some embodiments, the electrode assembly comprises one electrode(i.e., a working electrode). In some embodiments, the sensor includes atwo- or a three-electrode configuration. Thus, in some embodiments, theelectrode assembly comprises a working electrode and a referenceelectrode. In some embodiments, the electrode assembly comprises aworking electrode, a counter electrode, and a reference electrode.

The electrode assembly can further include one or more insulatingmaterials or components to physically contain at least a portion of theelectrode or electrodes, or to insulate electrodes from one another. Insome embodiments, the electrode assembly can comprise a coating toprotect the electrode or electrodes from the environment and/or toenhance the biocompatibility of the electrode assembly. For example, theelectrode assembly can comprise a biocompatible polymeric coatingcovering those portions of the assembly not covered by the gas permeablemembrane, so long as such coating does not interfere with the ability ofthe sensor to detect the gaseous species.

Suitable electrode materials include any electrically conductive metalsand other materials such as, but not limited to, platinum, palladium,rhodium, ruthenium, osmium, iridium, tungsten, nickel, copper, gold,silver, and carbon and carbon fibers, as well as, oxides, dioxides,combinations, or alloys thereof. In some embodiments, the electricallyconductive material is selected from carbon (including glassy carbon),carbon fibers, platinum (including platinized platinum), tungsten,silver, silver/silver chloride, gold, copper, indium tin oxide, iridiumoxide, nickel and combinations thereof. In some embodiments, the workingelectrode comprises a material selected from platinum, platinizedplatinum, tungsten, gold, carbon, carbon fiber, and combinationsthereof. In some embodiments, the reference electrode comprisessilver/silver chloride. In some embodiments, the counter electrodecomprises platinum.

The dimensions of the sensor can be varied to suit a particular use. Thepresently disclosed sensors include microsensors having a sensor tip(i.e., an area where the membrane-coated electrode assembly is exposedto the sample) with a diameter of between about 1 μm and about 1 mm. Insome embodiments, the microsensor has a sensor tip diameter of 1 μm orless. Microsensors having a sensor tip diameter of about 10 μm can alsobe referred to as “ultramicrosensors.” The presently disclosed sensorsalso include macrosensors, having a sensor tip diameter of about 1-10mm.

The sensors can be flexible or rigid. In some embodiments, the sensorscan include both rigid and flexible components. The inclusion of aflexible component can be based upon the desired end use of the sensor.For example, flexible components can be advantageous in the positioning,retrieval, and/or use of a sensor in vivo.

In some embodiments, the polysiloxane network is a condensation productof a silane mixture comprising an alkylalkoxysilane and a fluorosilane.The chemical structure and the relative amounts of the silanes in thesilane mixture can be varied to alter the biocompatibility, surfacewettability and porosity characteristics of the polysiloxane network,depending upon the intended use of the sensor.

In some embodiments, the sensor can further comprise an internalelectrolyte layer located between the electrode assembly or a portion ofthe electrode assembly and the gas permeable membrane. In someembodiments, the internal electrolyte layer is a hydrogel composition.Suitable hydrogels include hydrogels used in medical electrodes, suchas, but not limited to, hydrogel compositions comprising polyethyleneglycol (PEG), polyacrylamides,poly(2-arylamido-2-methyl-1-propanesulfonic acid) (polyAMPS), andpolyvinylpyrrolidone. In some embodiments, the hydrogel compositioncomprises polyvinylpyrrolidone.

In some embodiments, the sensor can be a Clark-type sensor, including aworking electrode and a reference electrode, each electrode insertedinto a separate barrel of a glass capillary tube. Suitable glasscapillary tubes are available, for example, from World PrecisionInstruments, Sarasota, Fla., United States of America). At the end ofthe capillary tube, the ends of the electrodes are exposed from theglass and are covered by the gas permeable membrane.

FIG. 1A shows a schematic illustration of a longitudinal cross view of arepresentative Clark-type sensor 100, which comprises a coating offluorosilane-based xerogel. The shaft of sensor 100 comprises electrodeassembly 102, which includes both working electrode 104 and referenceelectrode 106. The electrodes can be of any suitable electrode materialand can have any suitable dimensions to correspond to the desireddimensions of the electrode assembly and/or sensor as a whole. In someembodiments, the electrodes can have outer diameters ranging frombetween a few mm and a few tenths of a micrometer. Working electrode 104can comprise, for example, platinized Pt having an outer diameter of 127μm. Reference electrode 106 can comprise Ag/AgCl, having an outerdiameter of 250 μm. Thus, electrode assembly 102 can have an outerdiameter of, for example, 1.5 mm. Electrodes 104 and 106 are surroundedby insulating material 108 (e.g., borosilicate glass), which insulateselectrodes 104 and 106 from one another. End 110 of electrode assembly102 is covered by a layer of fluorosilane-based xerogel 112. Thus, toreach electrodes 104 and 106, any species from a sample that comes intocontact with sensor 100 must first diffuse through xerogel 112. Theother end of electrode assembly 102 (not shown) can be attached to thedetector. Sandwiched between electrodes 104 and 106 and xerogel 112 ishydrogel 114, which is optional.

FIG. 1B is a schematic illustration showing the view looking down on onelectrode assembly 102 at the surface of electrode assembly end 110. End104′ of working electrode 104 and end 106′ of working electrode 106 arenot covered by insulating material 108 at the surface of end 110.

FIGS. 2A-2C illustrate an example of a single microelectrode that couldbe covered with a fluorosilane-based xerogel according to the presentlydisclosed subject matter. More particularly, FIG. 2A shows a micrographimage of a tapered tungsten-platinum wire microelectrode comprising aplatinized end. As indicated in FIG. 2A, the diameter of the tapered,rougher, platinized region ranges from about 17 μm where the platinizedregion joins the smoother, unplatinized region of the microelectrode, toabout 5 μm at the tip of the microwire. The length of the platinizedregion is about 53 μm. FIG. 2B shows the platinized region of themicrowire under higher magnification, further illustrating the roughnessof the platinum black coating that results from the platinizationprocess. FIG. 2C is a schematic of the platinized region, which showsthat the microwire comprises a tungsten (W) core coated with a layer ofsmooth platinum (Pt). In the platinized region of the microwireelectrode, the smooth platinum layer is further coated with a roughlayer of platinum (i.e., platinum black). The roughness of the platinumblack layer can serve to increase the surface area of the platinizedregion.

III.A Sensor Formation

In some embodiments, the presently disclosed subject matter provides amethod of making a sensor for measuring an amount of a gaseous speciesin a sample, the method comprising:

(a) providing a silane mixture comprising a fluorosilane and analkylalkoxysilane;

(b) providing an electrode assembly;

(c) coating at least one portion of the electrode assembly with thesilane mixture to form a coated electrode; and

(d) drying the coated electrode to form a gas permeable polysiloxanemembrane layer on at least one portion of the electrode assembly.

In some embodiments, the silane mixture is dissolved in a solvent. Insome embodiments, the solvent comprises an alcohol and water. In someembodiments, the solvent comprises a catalyst, such as a Bronstead acidor base. In some embodiments, the catalyst is hydrochloric acid. Thus,in some embodiments, sol-gel chemistry techniques, such as describedhereinabove, provide readily useable methods for macro- and microsensorfabrication, as well as flexibility in optimizing the analyticalresponse characteristics of the sensor.

The electrode assembly can comprise one, two, three, or more electrodes.In some embodiments, the electrode assembly comprises one electrode(i.e., a working electrode). In some embodiments, the sensor includes atwo- or a three-electrode configuration. Thus, in some embodiments, theelectrode assembly comprises a working electrode and a referenceelectrode. In some embodiments, the electrode assembly comprises aworking electrode, a counter electrode, and a reference electrode. Theelectrode assembly can further include one or more insulating materialor component to physically contain at least a portion of the electrodeor electrodes, or to insulate the electrode from one another.

In some embodiments, the electrode assembly is a Clark-type electrodeassembly. In some embodiments, the electrode assembly is a single metalwire microelectrode or ultramicroelectrode. In some embodiments, thesingle metal wire microelectrode or ultramicroelectrode comprisesplatinized platinum or a platinized platinum/tungsten wire.

During the drying process, the solvent can be evaporated. Some dryingconditions can also be used to reduce the porosity of the membrane byleading to additional condensation of any remaining alkoxy and/orhydroxy groups in the network. Thus, in addition to varying thecomposition of the polysiloxane (e.g., ratio or the chemical compositionof the alkylalkoxysilane and the fluorosilane), the method of drying thecoated electrode assembly (e.g., the curing conditions) can be used tooptimize the sensitivity and selectivity of the sensor.

In some embodiments, the coated electrode assembly can be dried byexposure to ambient conditions for a period of time. Drying underambient conditions can be referred to as aging. Ambient conditionsinclude exposure to air or dry air (i.e., desiccated air) at roomtemperature (i.e., between about 20° C. and 25° C.) at atmosphericpressure. The coated electrode assembly can be aged for time periodsranging from several minutes (i.e., 5 min), to one or more hours, or toone to more days.

In some embodiments, the coated electrode assembly can be cured bydrying at an increased temperature (i.e., by annealing). For example,the coated electrode assembly can be cured at about 80° C. for a periodto time, such as several minutes to several hours.

Further, in some embodiments, the coated electrode assembly can be curedby exposure to a gas at a given pressure. For example, the coatedelectrode assembly can be cured by exposure to a gas, such as NO orargon gas, at a pressure between about 1 atm and about 5 atm for aperiod of time.

The curing or drying step of the presently disclosed methods can includeany combination of aging, annealing, or exposure to gas at a pressure.

The silane mixture can be coated onto the electrode assembly by anyconvenient method. For example, an aliquot of the silane mixture can beplaced onto a portion of the electrode assembly using a pipette,micropipette, syringe, or microsyringe. Alternatively, the electrodeassembly can be dipped into the silane mixture or into a solutioncomprising the silane mixture. The coating can be done manually or usinga robotic or otherwise mechanized device. The portion of the electrodeassembly coated will, in general, include at least a portion of theworking electrode.

The electrode assembly can be coated with as little as 0.02 μL/mm² ofthe silane coating mixture. In some embodiments, the membrane has athickness of between about 0.1 μm and about 10 μm.

In some embodiments, the thickness of the membrane layer can beoptimized for desired permeability or selectivity characteristics. Thus,in some embodiments, the coating or the coating and drying steps can berepeated one or more times to achieve a thicker membrane layer.

In some embodiments, the electrode assembly is coated with an internalelectrolyte layer prior to being coated with the silane mixture. In someembodiments, the electrolyte layer is a hydrogel composition, such as,for example, poly(vinylpyrrolidone). A hydrogel internal electrolytelayer can be formed by treating the electrode assembly with a mixturecomprising 30 mM sodium chloride, 0.3 mM hydrochloric acid, and 1%poly(vinylpyrrolidone) in water (pH=3.5). For example, the electrodeassembly can be dipped into the poly(vinylpyrrolidone) mixture and driedunder ambient conditions for 10 min prior to coating with the silanemixture. The thickness of such an internal electrolyte layer can be, forexample, approximately 1.5 μM.

III.B. Sensor Uses

In some embodiments, the presently disclosed subject matter provides amethod of measuring the amount of a gaseous species in a sample. Thesample can be a biological sample or an environmental sample. Inparticular, the presently disclosed sensors can be used to specificallyand quantitatively detect a gaseous species that is dissolved in asolution, such as an aqueous solution of biological media, either invitro or in vivo. Thus, in some embodiments, the sensor is a biosensor.In some embodiments, the gas is oxygen or nitric oxide. In particularembodiments, sensors provided by the presently disclosed subject mattercan detect nitric oxide.

In some embodiments, the sensors can detect and quantify nitric oxide oranother gaseous species present in a sample at low levels, for example,at levels as low as about 10 nM. In some embodiments, the gaseousspecies is present at a concentration as low as about 200 pM. Forexample, the sensors can selectively measure a gaseous species atconcentration levels between about 200 pM and about 4 μM. In someembodiments, the gaseous species is at a concentration of between about200 pM and about 300 nM. In some embodiments, the gaseous species is ata concentration of between about 200 pM and about 3 nM.

Thus, the presently disclosed sensors include nitric oxide sensors thatcan be used as research tools to investigate the biological actions ofNO, to monitor medical conditions related to NO-regulated processes, andto monitor the degradation, therapeutic, or adverse actions of a varietyof therapeutics, including the actions of NO-releasing therapeutics,such as nitroglycerin or amyl nitrite. NO-releasing therapeutics includethose which release NO themselves, as well as those which trigger therelease of NO by the body. In some embodiments, the presently disclosedsensors can be used as neurochemical research or medical diagnostictools.

In some embodiments, the biological sample in which the gas is beingmeasured is one of a cell, a tissue, an organ, or a biological fluid.Cells can include, for example, heart cells, brain cells, macrophagecells, neutrophil cells, monocyte cells, and endothelial cells.Biological fluids can include blood, plasma, gastric fluid, milk,saliva, cerebrospinal fluid (CSF) and the like. Biological samples canalso include cell cultures, tissue cultures and cell or tissue extracts.

In some embodiments, the sensors can be used to measure NO in the brainor in a brain cell or brain tissue. In some embodiments, the sensors canbe used to measure NO levels in blood, for example in a blood vessel. Insome embodiments, the sensors can be used to determine an immuneresponse by measuring NO in a macrophage cell, a neutrophil cell, or intissue comprising or believed to comprise a macrophage and/or neutrophilcell. In some embodiments, the sensors can be used to measure the NOconcentration in a single cell.

In some embodiments, the methods of the presently disclosed subjectmatter can be useful for measuring the concentration of nitric oxide (oranother biologically relevant gaseous species) in a biological samplederived from or present in a subject. In some embodiments, the subjectis a human subject, although it is to be understood that the subject canbe any living organism, including microbes, plants, and animals.

Accordingly, the term “subject” as used herein, refers to anyinvertebrate or vertebrate species. The methods and sensors of thepresently disclosed subject matter are particularly useful as diagnosticand research tools for use with samples from warm-blooded vertebrates.Thus, the presently disclosed subject matter concerns mammals and birds.More particularly, herein provided are methods for the study and/ordiagnosis of mammals, such as humans, as well as those mammals ofimportance due to being endangered (such as Siberian tigers), ofeconomical importance (animals raised on farms for consumption byhumans) and/or social importance (animals kept as pets or in zoos) tohumans, for instance, carnivores other than humans (such as cats anddogs), swine (pigs, hogs, and wild boars), ruminants (such as cattle,oxen, sheep, giraffes, deer, goats, bison, and camels), and horses. Alsoprovided is the study and diagnosis of birds, including those kinds ofbirds that are endangered, kept in zoos, as well as fowl, and moreparticularly domesticated fowl, e.g., poultry, such as turkeys,chickens, ducks, geese, guinea fowl, and the like, as they also are ofeconomical importance to humans. Thus, subjects include livestock,including, but not limited to, domesticated swine (pigs and hogs),ruminants, horses, poultry, and the like. Subjects also include animalsgenerally used in biological or medical research, such as rodents (e.g.,rats, mice and hamsters) and primates.

In some embodiments, the sample is derived from, but is no longerpresent in a living subject. Thus, in some embodiments, NO can bemeasured in a sample ex vivo. In some embodiments, the sample is presentin a living subject, and NO concentration can be measured in a sample invivo. In some embodiments, the sample is an environmental sample, suchas an air sample or a water sample taken from, for example, a lake, ariver, a stream, a pond, or any other outdoor water source. Thus, forexample, the presently disclosed sensors can be used to measure NOlevels in air, produced, for example, as waste from combustion enginesor power plants. The sensors can also be used to quantitate levels ofdissolved NO or O₂ in aquatic environments, to assess the ability ofsuch environments to sustain animal or plant life.

EXAMPLES

The following Examples have been included to provide guidance to one ofordinary skill in the art for practicing representative embodiments ofthe presently disclosed subject matter. In light of the presentdisclosure and the general level of skill in the art, those of skill canappreciate that the following Examples are intended to be exemplary onlyand that numerous changes, modifications, and alterations can beemployed without departing from the scope of the presently disclosedsubject matter.

Preparation and characterization of the presently disclosed networks,membranes, and sensors can be performed analogously to methods describedpreviously. See, for example, Shin, J. H., et al., Anal. Chem., 77,3494-3501 (2005), which is incorporated herein by reference in itsentirety. Silanes were obtained from Aldrich (Milwaukee, Wis., UnitedStates of America) or Gelest (Tullytown, Pa., United States of America).

Example 1 Permeability and Selectivity of Fluorosilane-Based Xerogels

Xerogel casting solutions were prepared by mixing 40 μL of MTMOS(Aldrich, Milwaukee, Wis., United States of America) and 10 μL offluorosilane (either (3,3,3-trifluoropropyl)trimethoxysilane (3FTMS),nonafluorohexyltrimethoxysilane (9FTMS),(tridecafluoro-1,1,2,2-tetrahydro-octyl)-trimethoxysilane (13FTMS) or(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane (17FTMS)) with200 μL ethanol (EtOH) and 100 μL water for 10 min. The synthesis of thexerogel was catalyzed by the addition of 10 μL of 0.5 M HCl. Thesolution was then deposited onto a platinized platinum workingmacroelectrode (platinized with a platinizing solution of 3%chloroplatinic acid and 0.1% lead acetate in water).

The permeability of the cured xerogels to NO and nitrite (NO₂ ⁻) wereevaluated electrochemically according to previously described proceduresby measuring the ratio of peak currents at the xerogel-coated and barePt electrodes in 10 μM NO and 100 μM nitrite solutions. See Shin, J. H.,et al., Anal. Chem., 77, 3494-3501 (2005). The selectivity of thexerogel-modified sensors for NO in the presence of nitrite wasdetermined using the separation solution method, also according topreviously described procedures. See Shin, J. H., et al., Anal. Chem.,77, 3494-3501 (2005).

The results of the permeability and selectivity testing are shown inFIG. 3. As indicated by the bar (medium gray) graph portion of FIG. 3,the xerogels comprising 3FTMS and 17FTMS had the highest NOpermeability. As indicated by the scatter graph (light colored squares)portion of FIG. 3, xerogels comprising 17FTMS were most effective atdiscriminating NO over NO₂ ⁻ under the noted conditions.

Example 2 Fluorosilane-Based Xerogel Membrane Microsensor

A casting solution was prepared by mixing 40 μL of MTMOS (Aldrich,Milwaukee, Wis., United States of America) and 10 μL(Heptadeca-fluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (Gelest,Tullytown, Pa., United States of America) with 200 μL ethanol (EtOH) and100 μL water for 10 min. The synthesis of the xerogel was catalyzed bythe addition of 10 μL of 0.5 M HCl. The solution was then deposited ontoa platinized platinum working microelectrode (platinized with aplatinizing solution of 3% chloroplatinic acid and 0.1% lead acetate inwater).

After curing, NO response and calibration curves for thexerogel-modified microelectrode were obtained by injecting aliquots of astandard NO solution (1.9 mM) into 100 mL phosphate buffered saline(PBS, pH 7.4) at room temperature under constant stirring. Amperometricmeasurements were performed using a CH Instruments 660A potentiostat (CHInstruments, Inc., Austin, Tex., United States of America). Currentswere recorded at an applied potential of +0.8 V (vs an Ag/AgCl referenceelectrode). The xerogel-modified microelectrode was prepolarized for atleast 30 min prior to use.

FIG. 4 shows the response and calibration curve (inset) for the modifiedmicroelectrode over an NO concentration range of 30 nM to 1200 nM. Eachdrop in the dynamic response curve indicates the addition of an aliquotof the NO solution. The response of the modified microelectrode was alsoassayed for the potentially interfering molecular species, nitrite (NO₂⁻). As shown in the dynamic response curve, after about 450 sec,aliquots of a solution of nitrite were added to the PBS solution, todetermine the response of the modified microelectrode to nitrite atconcentrations between 2 μM and 25 μM. The nitrite solution was preparedfrom sodium nitrite (Sigma Chemical Co., St. Louis, Mo., United Statesof America). As indicated in FIG. 4 (and as expected based on the datadescribed in Example 1), the coated microelectrode appeared to besignificantly less sensitive to nitrite than to NO.

FIG. 5 shows an expansion of the response curve and calibration curve(inset) from FIG. 4 at NO concentrations between 30 nM and 300 nM. Thecalibration curve shows that the coated microelectrode has a linearresponse to NO concentrations between 30 nM and 300 nM (slope of −9.96pA/nM; r=0.9987). The slope of the calibration curve corresponds to theresponse sensitivity of the coated microelectrode.

FIG. 6A shows the dynamic response curve for the coated microelectrodeto NO concentrations between 0.5 μM and 4.0 μM. The slope of thecorresponding calibration curve (shown in FIG. 6B) is −7.60 nA/mM(r=0.9999). In comparison, the dynamic response curve and calibrationcurve of a non-coated microelectrode (i.e., a bare platinized platinumelectrode) to NO in the same concentration range are shown in FIGS. 7Aand 7B. The slope of the calibration curve of the bare platinizedplatinum electrode is −11.57 nA/mM (r=9999).

FIG. 8 shows the dynamic response curve and calibration curve (inset)for the coated microelectrode at nitric oxide concentrations between 200pM and 3 nM. The right-hand side of the dynamic response curve alsoshows the response of the coated microelectrode to NO₂ ⁻ atconcentrations between 1 μM and 5 μM.

Example 3 Oxygen Response of Fluorosilane-Based Xerogel-Coated Sensors

A membrane-coated macroelectrode sensor was prepared using a membranecasting solution comprising 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane and 80% byvolume methyltrimethoxysilane (MTMOS). The casting solution was preparedas described in Example 2, above. The sensor comprised a three-electrodeassembly configuration having a Pt working electrode (2 mm), a Pt wirecounter electrode (0.6 mm) and an Ag/AgCl (3.0 M KCl) referenceelectrode.

Oxygen response and calibration curves were obtained using previouslydescribed methods. See Marxer, S. M. et al., Analyst, 130, 206-212(2005). More particularly, the membrane-coated electrode assembly wasplaced into phosphate-buffered saline (PBS) solutions saturated with 0,36, 72, 151, or 360 mmHg O₂. The PBS solutions were at room temperatureand were constantly stirred. Amperometric measurements were performedusing a CH Instruments 660A potentiostat (CH Instruments, Inc., Austin,Tex., United States of America). Currents were recorded at an appliedpotential of −0.65 V (vs an Ag/AgCl reference electrode).

Oxygen response and calibration curves are shown in FIG. 9. As indicatedby the calibration curve, the membrane-coated macroelectrode had alinear response to O₂ at concentrations between 36 mmHg and 360 mmHg.

Example 4 Biocompatibility of Fluorosilane-Based Xerogel Membranes

The biocompatibility of the presently disclosed fluorosilane-basedxerogel membranes was determined by assessing the membranes' ability toresist platelet adhesion. Platelet adhesion resistance was determinedaccording to previously disclosed methods. See Marxer, S. M., et al.,Analyst, 130, 206-212 (2005).

More particularly, acid citrate dextrose (ACD)-anticoagulated porcineblood (3 parts ACD to 20 parts whole blood) was centrifuged at 200×g for30 min at room temperature to obtain platelet rich plasma (PRP). Calciumchloride was added to the PRP to a final concentration of 0.25-0.50 mMCa²⁺ to maintain normal platelet activity. Fluorosilane-based xerogelmembrane-coated glass slides were immersed in the PRP for 1 hour at 37°C. in a humid environment. The slides were rinsed with Tyrode's buffer(pH 7.4) to remove loosely adhered platelets. The attached plateletswere then fixed with a 1% glutaraldehyde solution (v/v, Tyrode's buffer)for 30 min. The slides were rinsed with Tyrode's buffer and water andchemically dried by immersion in 50%, 75%, and 95% ethanol (v/v, water)for 5 min each, followed by immersion in 100% ethanol for 10 minutes andfinally in hexamethyldisilazane for about 12 hours.

Phase contrast images of the slides were obtained using a Zeiss Axiovert200 inverted microscope (Carl Zeiss MicroImaging, Inc., Chester, Va.,United States of America). The amount of platelet adhesion on thexerogel membrane-coated slides was compared relative to that ofnon-coated glass slides. The relative platelet adhesion of afluorosilane-based xerogel membrane-coated glass slide prepared from acasting solution comprising a silane mixture of 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane and 80% byvolume MTMOS is shown in FIG. 10 (right-hand bar, indicated by 17FTMS).Relative platelet adhesion to a xerogel membrane-coated glass slideprepared from a casting solution comprising a single silane, MTMOS, isalso shown in FIG. 10 (left-hand bar, indicated by MTMOS).

REFERENCES

The references listed below as well as all references cited in thespecification are incorporated herein by reference to the extent thatthey supplement, explain, provide a background for or teach methodology,techniques and/or compositions employed herein. All cited patents andpublications referred to in this application are herein expresslyincorporated by reference.

-   Marxer, S. M., et al., Analyst, 130, 206-212 (2005).-   Shin, J. H., et al., Anal. Chem., 77, 3494-3501 (2005).-   Zhang, X., Frontiers in Bioscience, 9, 3434-3446 (2004).

It will be understood that various details of the presently disclosedsubject matter can be changed without departing from the scope of thepresently disclosed subject matter. Furthermore, the foregoingdescription is for the purpose of illustration only, and not for thepurpose of limitation.

1. A sensor for measuring an amount of a gaseous species in a sample,the sensor comprising: (a) an electrode assembly; (b) a gas permeablemembrane located between one or more surfaces of the electrode assemblyand the sample, wherein the membrane comprises a polysiloxane networkwherein one or more silicon atoms in the polysiloxane network iscovalently attached to an alkyl group and one or more silicon atoms inthe polysiloxane network is covalently attached to a fluorinated alkylgroup; and (c) a detector for measuring current at the electrodeassembly.
 2. The sensor of claim 1, wherein the gaseous species isselected from nitric oxide and oxygen.
 3. The sensor of claim 1, whereinthe electrode assembly is selected from the group consisting of: anelectrode assembly comprising a working electrode; an electrode assemblycomprising a working electrode and a reference electrode; and anelectrode assembly comprising a working electrode, a referenceelectrode, and a counter electrode.
 4. The sensor of claim 3, whereinthe working electrode is selected from platinum, platinized platinum,tungsten, gold, carbon, carbon fiber, and combinations thereof.
 5. Thesensor of claim 3, wherein the reference electrode comprisessilver/silver chloride.
 6. The sensor of claim 3, wherein the counterelectrode comprises platinum.
 7. The sensor of claim 1, wherein thepolysiloxane network is a condensation product of a silane mixturecomprising an alkylalkoxysilane and a fluorosilane.
 8. The sensor ofclaim 7, wherein the fluorosilane comprises a structure having aformula:F₃C(CF₂)_(m)—(CH₂)_(n)—Si(X)_(p)(Y)_(3-p) wherein: m is 0 to 15; n is 1to 5; p is 1, 2, or 3; each X is independently selected from the groupconsisting of alkoxy, aryloxy, aralkoxy, hydroxyl, and halo; and each Yis independently selected from the group consisting of H, alkyl, aryl,and aralkyl.
 9. The sensor of claim 8, wherein the fluorosilane isselected from the group consisting of:(3,3,3-trifluoropropyl)trimethoxysilane;nonafluorohexyltrimethyoxysilane; nonafluorohexyltriethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane;(perfluoroalkyl)ethyltriethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane; andcombinations thereof.
 10. The sensor of claim 7, wherein thealkylalkoxysilane is selected from the group consisting of:methyltrimethoxysilane (MTMOS); ethyltrimethoxysilane;propyltrimethoxysilane; butyltrimethoxysilane (BTMOS);hexyltrimethoxysilane (HTMOS); octyltrimethoxysilane (OTMOS); andcombinations thereof.
 11. The sensor of claim 7, wherein the silanemixture comprises about 1% to about 99% by volume fluorosilane.
 12. Thesensor of claim 11, wherein the silane mixture comprises about 5% toabout 50% by volume fluorosilane.
 13. The sensor of claim 12, whereinthe silane mixture comprises about 20% by volume fluorosilane.
 14. Thesensor of claim 13, wherein the silane mixture comprises about 20% byvolume (heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxy-silane andabout 80% by volume methyltrimethoxysilane.
 15. The sensor of claim 1,wherein the sensor further comprises an internal electrolyte layer,wherein the internal electrolyte layer is located between the electrodeassembly and the gas permeable membrane.
 16. The sensor of claim 15,wherein the internal electrolyte layer is a hydrogel composition. 17.The sensor of claim 16, wherein the hydrogel composition comprisespoly(vinylpyrrolidone).
 18. A method of making a sensor for measuring anamount of a gaseous species in a sample, the method comprising: (a)providing a silane mixture comprising a fluorosilane and analkylalkoxysilane; (b) providing an electrode assembly; (c) coating atleast one portion of the electrode assembly with the silane mixture toform a coated electrode; and (d) drying the coated electrode to form agas permeable polysiloxane membrane layer on at least one portion of theelectrode assembly.
 19. The method of claim 18, wherein the fluorosilanecomprises a structure having a formula:F₃C—(CF₂)_(m)—(CH₂)_(n)—Si(X)_(p)(Y)_(3-p) wherein: m is 0 to 15; n is 1to 5; p is 1, 2, or 3; each X is independently selected from the groupconsisting of alkoxy, aryloxy, aralkoxy, hydroxyl, and halo; and each Yis independently selected from the group consisting of H, alkyl, aryl,and aralkyl.
 20. The method of claim 19, wherein the fluorosilane isselected from the group consisting of:(3,3,3-trifluoropropyl)trimethoxysilane;nonafluorohexyltrimethyoxysilane; nonafluorohexyltriethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane;(perfluoroalkyl)ethyltriethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane; andcombinations thereof.
 21. The method of claim 18, wherein thealkylalkoxysilane is selected from the group consisting of:methyltrimethoxysilane (MTMOS); ethyltrimethoxysilane;propyltrimethoxysilane; butyltrimethoxysilane (BTMOS);hexyltrimethoxysilane (HTMOS); octyltrimethoxysilane (OTMOS); andcombinations thereof.
 22. The method of claim 18, wherein the silanemixture comprises about 1% to about 99% by volume fluorosilane.
 23. Themethod of claim 22, wherein the silane mixture comprises about 5% toabout 50% by volume fluorosilane.
 24. The method of claim 23, whereinthe silane mixture comprises about 20% by volume fluorosilane.
 25. Themethod of claim 24, wherein the silane mixture comprises about 20% byvolume (heptadecafluoro-1,1,2,2-tetrahydrodecyl)-triethoxysilane and 80%by volume methyltrimethoxysilane.
 26. The method of claim 18, whereinthe silane mixture is dissolved in a solvent.
 27. The method of claim26, wherein the solvent comprises an alcohol and water.
 28. The methodof claim 27, wherein the alcohol is ethanol.
 29. The method of claim 26,wherein the solvent further comprises a catalyst.
 30. The method ofclaim 29, wherein the catalyst is hydrochloric acid.
 31. The method ofclaim 18, wherein the electrode assembly is selected from the groupconsisting of: an electrode assembly comprising a working electrode; anelectrode assembly comprising a working electrode and a referenceelectrode; and an electrode assembly comprising a working electrode, areference electrode, and a counter electrode.
 32. The method of claim31, wherein the working electrode is selected from platinum, platinizedplatinum, tungsten, gold, carbon, carbon fiber, and combinationsthereof.
 33. The method of claim 31, wherein the reference electrodecomprises silver/silver chloride.
 34. The method of claim 31, whereinthe counter electrode comprises platinum.
 35. The method of claim 18,wherein the drying takes place at ambient temperature.
 36. The method ofclaim 18, wherein the drying takes place at an elevated temperature. 37.The method of claim 18, wherein the drying step comprises exposing themembrane layer to one of nitric oxide or argon at a pressure.
 38. Themethod of claim 18, wherein the coating is performed by dipping theelectrode assembly into the silane mixture.
 39. The method of claim 18,further comprising repeating the coating and drying steps one or moretimes to provide a thicker membrane layer.
 40. The method of claim 18,wherein prior to coating the at least one portion of the electrodeassembly with the silane mixture, the at least one portion of theelectrode assembly is coated with a hydrogel material.
 41. A sensorprepared by the method of claim
 18. 42. A method of measuring an amountof a gaseous species in a sample, the method comprising contacting thesample with a sensor comprising a polysiloxane membrane; wherein: thepolysiloxane membrane comprises one or more silicon atoms covalentlyattached to an alkyl group and one or more silicon atoms covalentlyattached to a fluorinated alkyl group; and the polysiloxane membraneselectively allows the gaseous species in the sample to be measured bythe sensor.
 43. The method of claim 42, wherein the polysiloxanemembrane is a condensation product of a silane mixture comprising analkyl alkoxysilane and a fluorosilane.
 44. The method of claim 42,wherein the sensor is an amperometric sensor.
 45. The method of claim44, wherein the polysiloxane membrane is positioned between the sampleand an electrode assembly.
 46. The method of claim 45, wherein theelectrode assembly is selected from the group consisting of: a electrodeassembly comprising a working electrode; an electrode assemblycomprising a working electrode and a reference electrode; and anelectrode assembly comprising a working electrode, a referenceelectrode, and a counter electrode.
 47. The method of claim 42, whereinthe sample is a biological sample or an environmental sample.
 48. Themethod of claim 47, wherein the sample is a biological sample selectedfrom the group consisting of a cell, a tissue, a biological fluid, andextracts thereof.
 49. The method of claim 48, wherein the sample isselected from brain tissue, a brain cell, or blood.
 50. The method ofclaim 48, wherein the sample is in a living subject.
 51. The method ofclaim 50, wherein the sample is in the brain of a living subject. 52.The method of claim 42, wherein the gaseous species is selected from thegroup consisting of nitric oxide and oxygen.
 53. The method of claim 42,wherein the gaseous species is present in the sample at a concentrationas low as about 200 pM.
 54. A composition comprising a polysiloxanenetwork, wherein one or more silicon atoms in the polysiloxane networkis covalently attached to an alkyl group and one or more silicon atomsin the polysiloxane network is covalently attached to a fluorinatedalkyl group having a structure of:

wherein m is 0 to 15 and n is 1 to
 5. 55. The composition of claim 54,wherein each silicon atom in the polysiloxane network is covalentlyattached to an alkyl group or to a fluorinated alkyl group.
 56. Thecomposition of claim 54, wherein the polysiloxane network is selectivelypermeable for a biologically relevant gaseous species.
 57. Thecomposition of claim 56, wherein the biologically relevant gaseousspecies is selected from the group consisting of nitric oxide andoxygen.
 58. The composition of claim 54, wherein the polysiloxanenetwork is a condensation product of a silane mixture comprising analkylalkoxysilane and a fluorosilane.
 59. The composition of claim 58,wherein the fluorosilane comprises a structure having a formula:F₃C—(CF₂)_(m)—(CH₂)_(n)—Si(X)_(p)(Y)_(3-p) wherein: m is 0 to 15; n is 1to 5; p is 1, 2, or 3; each X is independently selected from the groupconsisting of alkoxy, aryloxy, aralkoxy, hydroxyl, and halo; and each Yis independently selected from the group consisting of H, alkyl, aryl,and aralkyl.
 60. The composition of claim 59, wherein the fluorosilaneis selected from the group consisting of:(3,3,3-trifluoropropyl)trimethoxysilane;nonafluorohexyltrimethyoxysilane; nonafluorohexyltriethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane;(tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trimethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane;(perfluoroalkyl)ethyltriethoxysilane;(heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane; andcombinations thereof.
 61. The composition of claim 58, wherein thealkylalkoxysilane is selected from the group consisting of:methyltrimethoxysilane (MTMOS); ethyltrimethoxysilane;propyltrimethoxysilane; butyltrimethoxysilane (BTMOS);hexyltrimethoxysilane (HTMOS); octyltrimethoxysilane (OTMOS); andcombinations thereof.
 62. The composition of claim 58, wherein thesilane mixture comprises about 1% to about 99% by volume fluorosilane.63. The composition of claim 62, wherein the silane mixture comprisesabout 5% to about 50% by volume fluorosilane.
 64. The composition ofclaim 63, wherein the silane mixture comprises about 20% by volumefluorosilane.
 65. The composition of claim 64, wherein the silanemixture comprises about 20% by volume(heptadecafluoro-1,1,2,2-tetrahydrodecyl)-triethoxysilane and about 80%by volume methyltrimethoxysilane.
 66. The composition of claim 58,wherein the silane mixture is dissolved in a solvent comprising analcohol and water.
 67. The composition of claim 66, wherein the solventfurther comprises a catalyst.
 68. The composition of claim 67, whereinthe catalyst is hydrochloric acid.
 69. The composition of claim 66,wherein the polysiloxane network is formed by a sol-gel process.